Martindale Abrasion And Pilling Tester can be used to determine the textile resistance to pilling and other changes on its surface, this method is applicable to all textiles, especially suitable for woven fabrics. This test method is not applicable to fabrics with a thickness of more than 3mm, because this kind of cloth clip sample holder is not tight, Shanghai Qianshui Precision Electromechanical Technology Co.

Martindale Abrasion And Pilling Tester before the need to do the relevant preparatory work, in order to more accurate experiments to produce relevant results, QINSUN instrument technical engineers briefly summarized as follows.

Experimental sampling:

1, initial sampling: generally selected from the rolled fabric samples.

2、Laboratory sampling: take a whole cloth sample from the rolled sample, note that the outer 1 yard of cloth should be discarded first.

Test samples：

Selection, quantity and preparation

1、In addition to other instructions, before cutting the test sample should be pre-washed or dry-cleaned, according to the end use of the fabric to adjust the moisture, the specific can also be negotiated by both sides.

2, from each laboratory to cut a pair of round specimens, respectively, 38mm and 140mm in diameter.

3, laboratory samples of the whole sample, for clothing can be sampled along different cut pieces, sampling should be staggered sampling, so that the samples taken will not have the same warp and weft. Sampling should avoid wrinkling or other deformation, in addition to other provisions, the cut sample can not be close to the edge of the cloth within 1 / 10 sampling.

Experimental moisture conditioning.

The specimen should be humidified for at least 4 hours under the standard environment with the temperature of 21±1℃ and relative humidity of 65±2%.

The above is QINSUN instrument for you to answer the details of the detailed content, hope to help you, of course, if you want to buy products welcome you to come to consult.